DP steels were extensively used in the vehicles industry due to its extraordinary combined properties of strength, ductility, formability and weldability which contributed great significance in reducing strength to weight ratio and CO2 emission. High strength steel i.e. DP steels (3 different grades) were experimentally investigated and thermophysically simulated using Gleeble 3500 simulator to determine softening and hardening in heat affected zone. Samples were heated to different peak temperatures (1350 °C, 950 °C, 775 °C and 650 °C), two cooling time (t8.5/5 = 5 s and 30 s) and Rykalin 2D model were selected. The hardness and microstructure of the specimens were tested and analysed. For longer cooling time (t8.5/5= 30 s), we observed that softening occurs in all grade of investigated DP steels to all sub-regions. But for shorter cooling time i.e. t8.5/5= 5 s the softening is higher in intercritical HAZ compared to other sub-regions for all the types of DP steel with short cooling time (t8.5/5 = 5 s). However, the hardening zone in the CGHAZ occurs when Tmax is 1350 ºC for DP600, DP800 & DP1000 steels but it is more prominent in DP800 as compared to others two steel grade.