ABSTRACTA simulated Magnox glass which is Mg- and Al- rich was subjected to aqueous corrosion in static mode with deionised water at 90 °C for 7-28 days and assessed using X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) with Energy X-Ray Dispersive Spectroscopy (EDS) and Inductively Coupled Plasma – Optical Emission Spectroscopy (ICP-OES). XRD revealed both amorphous phase and crystals in the glass structure. The crystals were Ni and Cr rich spinels and ruthenium oxide. After two weeks of incubation in deionised water, the glass surface was covered by a ∼11 μm thick Si-rich layer whilst mobile elements and transition metals like Na, B, and Fe were strongly depleted. The likely corrosion mechanism and in particular the role of Mg and Al in the glass structure are discussed.