La0.75Sr0.25Cr0.5-xMn0.5TixO3 (x = 0.1, 0.2) has been synthesized in solid state reaction method and tested as a potential anode material for solid oxide fuel cells. Rietveld refinement of X-ray powder diffraction data using Fullprof software shows that the materials crystallize in the rhombohedral symmetry in the R-3C space group. The cell parameters are: a = b = 5.5286 (4) A, c = 13.408(1) A, α = β = 90°, γ = 120°. Particle size distribution measurements show that the average particle size for x = 0.1 and 0.2 was 232.66 nm and 176.63 nm, respectively. The potential on particles were found to be −22.86 mV and −27.73 mV, for x = 0.1 and x = 0.2, respectively. Thermal expansion measurement using thermo-mechanical analyzer shows that the thermal expansion coefficient is 13.96 × 10−6/°C which is close to the thermal expansion of the state-of–the art YSZ electrolyte. Microstructure has been observed from scanning electron microscopy which shows a porous structure. Energy dispersive X-ray shows that the percen...