It is demonstrated that titanium carbide powder can be obtained from titanium swarf. The following optimum parameters of carbidization in a vacuum corresponding to 0.013 Pa have been established: 1.5-h holding at a temperature of 1873°K; 0.5-h holding at 2273°K; 0.5-h comminution in a vibratory mill; and 0.5-h holding at 2273°K, The amount of oxygen in the titanium carbide powder produced was found to be less than that in the powder currently manufactured in the Soviet hard-metal industry.