The specific electrical strength of carbonic heat-insulating charge influences considerably the uniformity of electric power distribution in the volume of graphitization furnace that determines the quality of the product and production costs. The article comprises the review of existing information on specific electrical strength of carbonic bulk materials and the methods of their testing. Existing literary information does not confirm with the specific technological conditions in graphitization furnaces. That is why the high-temperature device was made to measure the specific electrical strength of carbonic materials with the particle distribution from 0 to 20 mm and within the applied pressure 1 – 50 kPa. The results obtained are represented as diagrams which show barometric dependence of specific electrical strength for carbon residue with the particles’ size below 10 mm, the temperature dependence of specific electrical strength for unary carbonic mixture with various proportions of raw and tempered carbonic residue, the temperature dependence of the specific electrical strength of raw carbonic residue with diverse size of particles.

Разработана установка для измерения удельного электрического сопротивления сыпучих углеродных материалов гранулометрическим составом от 0 до 20 мм в температурном диапазоне 20 – 1000 °С. Получены данные удельного электрического сопротивления однокомпонентной шихты с различными пропорциями ее составляющих и различного фракционного состава.

Розроблена установка для вимірювання питомого електричного опору сипучих вуглецевих матеріалів гранулометричним складом від 0 до 20 мм в температурному діапазоні 20 – 1000 °С. Отримані дані питомого електричного опору однокомпонентної шихти з різними пропорціями її складових та різного фракційного складу.