AbstractHigh purity amorphous silicon layers were obtained by ultrahigh vacuum (millitorr range) chemical vapor deposition (UHVCVD) from disilane gas. The crystalline fraction of the films was monitored by in situ electrical conductance measurements performed during isothermal annealings. The experimental conductance curves were fitted with an analytical expression, from which the characteristic crystallisation time, tc, was extracted. Using the activation energy for the growth rate extracted from our previous work, we were able to determine the activation energy for the nucleation rate for the analysed-films. For the films including small crystallites we have obtained En ∼ 2.8 eV, compared to En ∼ 3.7 eV for the completely amorphous ones.