The authors acknowledge financial support from the Spanish Ministerio de Educación y Ciencia for the financial support in the form of Ramón y Cajal contracts (RyC 2002 and 2004 respectively). Some of this work was carried out under the auspices of an EPSRC/MOD sponsored project on bainitic steels at the University of Cambridge; we are extremely grateful for this support over a period of three years. The authors are extremely grateful to Prof. H. K. D.

Novel bainitic microstructures, consisting of slender ferrite plates (tens of nm) in a matrix of retained austenite, have reported maximum yield strength of 1.4 GPa, ultimate tensile strength of 2.2 GPa, 30% ductility and respectable levels of fracture toughness (∼51 MPa m0.5). The unusual combination of properties is attributed to the fine bainitic plates and the presence of retained austenite in the microstructure.