To chemically prepare polypyrrole(pPy) coated fabrics(silk, cotton and nylon fabrics), the fabrics were first soaked in 0.4M oxidant /0.06M dopant anthraquinone-2-sulfonic acid solution for 5min at room temperature, and subsequently soaked in a 0.4M monomer pyrrole aqueous solution for 5min at room temperature. The content(wt%) of coated pPy in the coated fabrics was controlled by the number of treatments(these two steps). This study examined the effect of the number of treatments/pPy content on the sheet resistance, mechanical/bending properties and color behaviors of pPy coated fabrics. The coated pPy content, sheet resistance(/square) and color strength(K/S) of pPy coated fabrics increased sharply with increasing number of treatments up to 20 times, while the increase slowed down afterward. The tensile strength, elongation at break and lightness() decreased with increasing number of treatments. The tensile modulus and bending rigidity of coated fabrics increased significantly with increasing number of treatments/coated pPy content. This indicated that the flexibility of coated fabrics decreased considerably.