This study evaluates Vickers microhardness and surface roughness in Biodentine cement (M1) and glass-ionomer cement Fuji IX (M2), both immersed in mouthwash.Fifty-four samples were randomly distributed in distilled water (S1), Listerine Cool Mint (S2), and Colgate Plax (S3). Each sample was put in a flask with mouthwash for 2 min, under vibration, twice a day for 21 days. Microhardness and surface roughness were assessed at 48 h (T0), 7 days (T1), 14 days (T2), and 21 days (T3).For roughness: time (T), solution (S) and material (M), TxM, and SxM and for microhardness: M, TxS, TxM, and SxM were statistically significant. T3, M1, M1T3, and M1S1 presented the highest surface roughness. M2, M1T0, M1T1, M1T2, M1S1, and M1S2 presented higher microhardness.Biodentine showed higher surface roughness for T1, T2, and T3 and higher microhardness for T0, T1, and T2 against Fuji IX. Biodentine presented higher microhardness independently of solution.