This paper investigates the evolution of microstructure and its related mechanical properties of Q-P processed medium-carbon AHSS steel. The investigated informations were compared to the structures and mechanical properties of quenched and tempered, austempered specimens made of the same steel grade. According to the correlations between observed microstructures after Q-P, quenching and tempering, austempering the presence of bainite in Q-P processed specimens was found. The hypothesis of bainite growth durinq Q-P processing was devoleped. The experimental results show that during Q-P heat treatment the bainite transformation can occur even when the partitioning temperatures are below the temperature Ms of experimental steel.

Tento článek se zabývá vývojem mikrostruktury a s ní souvisejících mechanických vlastností středněuhlíkové AHSS oceli zpracované metodou Q-P. Zkoumané aspekty byly porovnány se strukturou a mechanickými vlastnostmi kalených a popuštěných, austemperovaných vzorků vyrobených ze stejné třídy oceli. Podle korelací mezi pozorovanými mikrostrukturami po Q-P procesu, kalení a popouštění a austemperaci byla zjištěna přítomnost bainitu ve vzorcích zpracovaných Q-P procesem. Byla navržena hypotéza o růstu bainitu během Q-P zpracování. Experimentální výsledky ukazují, že během tepelného zpracování Q-P může dojít k přeměně bainitu, i když jsou teploty přerozdělení nižší než teplota Ms experimentální oceli.