ABSTRACTFirst, fatigue tests were performed on butt‐welded joints made of novel direct quenched ultra high strength steel with high quality welds. Two different welding processes were used: MAG and Pulsed MAG. The weld profiles, misalignments and residual stresses were measured, and the material properties of the heat‐affected zone were determined. Fatigue tests were carried out with constant amplitude tensile loading both for joints in as‐welded condition and for joints after ultrasonic peening treatment. Finally, in fatigue strength predictions, the crack initiation phase was estimated using the procedures described by Lawrence et al. [Lawrence F V, Ho N J and Mazumdar P K (1981) Predicting the fatigue resistance of welds. Annu. Rev. Mater. Sci, 11, 401–425]. The propagation phase was simply estimated using S–N curves for normal quality butt welds, which may contain pre‐existing cracks or crack‐like defects eliminating the crack initiation stage.