Conventional glass ionomer cement (GIC) is among the mostly used material in dentistry but some modifications were needed due to its deficiencies such as low mechanical strength and opacity. In this study, a new nanocomposite, GIC-nanoSiO2-HA-ZrO2 was fabricated whereby zirconia is added to improve the hardness. The nanocomposite of SiO2-HA-ZrO2 was synthesized using two different mixing methods which are one pot and spatulation methods. One pot method involved the addition of zirconia nanopowder during the one pot synthesis of nanoSiO2-HA and spatulation method involved the addition of zirconia nanopowder by controlled grinding process using mortar and pestle. Different weight percentage from 1-20 % of nanoSiO2-HA-ZrO2 was added to GIC and the hardness was analyzed using Vickers Tester. The one pot method recorded the highest and significant hardness value at 3 % addition which is ∼75.27 HV (± 2.48) compared to spatulation method ∼69.53 HV (± 7.78) at p < 0.05. Scanning Electron Microscope image from one...