Abstract Tungsten powder (0.6–0.9 μm) was sintered by field assisted sintering technology (FAST) at various processing conditions. The sample sintered with in-situ hydrogen reduction pretreatment and pulsed electric current during heating showed the lowest amount of oxygen. The maximum relative density achieved was 98.5%, which is from the sample sintered at 2000 °C, 85 MPa for 30 min. However, the corresponding sintered grain size was 22.2 μm. To minimize grain growth, nano tungsten carbide powder (0.1–0.2 μm) was used as sintering additive. By mixing 5 and 10 vol.% WC with W powder, densification was enhanced and finer grain size was obtained. Relative density above 99% with grain size around 3 μm was achieved in W–10 vol.% WC sintered at 1700 °C, 85 MPa, for 5 min.