The recent field experience and several experimental results have shown the possible deleterious effect of a heat affected zone (HAZ) induced by welding on the susceptibility to the stress corrosion cracking (SCC) of Alloy 600 of bottom penetrations exposed to primary water of PWRs. This work tried to quantify the increasing susceptibility to initiation and crack propagation in 600/182 HAZ. The rolled plate did not exhibit any susceptibility to SCC except for a cold work higher than 10% typically. By contrast, the weld metal was well known for its high susceptibility to SCC. Metallurgical and mechanical characterizations of the HAZ indicated a slight gradient of Vickers micro hardness close to the fusion line (up to few mm) and a lack of intergranular precipitates up to 500 µm from the fusion line. SCC tests clearly demonstrated that a non-susceptible plate may exhibit a significant susceptibility to SCC propagation in the HAZ. Results of initiation tests did not allow to observe any SCC in the base metal, due to the high susceptibility to SCC of the weld.