It was established that a polymeric film deposited on a glassy carbon electrode from nickel(II) tetrasulfonated phthalocyanine solution shows electrocatalytic activity during oxidation of cysteine. A decrease in its oxidation potential and a multiple increase in the oxidation current were observed compared to the unmodified electrode. The conditions for the polymeric film preparation on the surface of glassy carbon electrode and the recording of the maximal catalytic current on this electrode were determined. The linear dependence of current value on cysteine concentration was observed up to 1·10-6 and 1·10-7 mol/l under static and flow conditions.

Установлено, что полимерная пленка, осажденная на поверхности стеклоуглеродного электрода из раствора тетрасульфофталоцианина никеля(II), проявляет электрокаталитическую активность при окислении цистеина. По сравнению с немодифицированным электродом наблюдается уменьшение потенциала окисления и многократное увеличение тока окисления органического соединения. Найдены рабочие условия получения полимерной пленки на поверхности стеклоуглерода и регистрации максимального каталитического тока на этом электроде. Линейная зависимость величины тока от концентрации цистеина наблюдается до 1·10-6 и до 1·10-7моль⋅л-1 в стационарных и проточных условиях.