There is shown the possibility of increasing the complex of concrete mixture and concrete physical-and-technical properties when using an organic-mineral modifier that affects significantly physical-and-chemical processes of binders hardening. The optimum composition of the organic-mineral modifier was determined. To obtain the modifier there were used various organic and inorganic compounds. Comparative experiments were conducted with a super-plasticizer and water-repellent plasticizing additive to study the effect of the water-repellent organic-mineral agent on cement materials quality. The analysis results showed that strength of the concrete with the organic-mineral modifier was 1,7 to 1,8 higher as compared to the concrete without additives and 50 % higher as compared to the concrete with other modifiers. High prism strength of the concrete with the organic-mineral modifier (it exceeds more than 1,5 times the concrete composition without the modifier) indicates its crack growth resistance.

Показана возможность повышения комплекса физико-технических свойств бетонной смеси и бетона при использовании органоминерального модификатора, который существенно влияет на физико-химические процессы твердения вяжущих. Были определены оптимальные составы органоминерального модификатора. Для получения модификатора используются различные органические и неорганические соединения. Для исследования влияния гидрофобизирующего органоминерального модификатора на качество цементных материалов были проведены сравнительные опыты с суперпластификатором и гидрофобно-пластифицирующей добавкой. Анализ результатов показал, что прочность бетона с органоминеральным модификатором выше в 1,7–1,8 раза в сравнении с бетоном без добавок и на 50 % выше со сравниваемым бетоном с другими модификаторами. Высокая призменная прочность бетона с органоминеральным модификатором (она превышает более чем в 1,5 раза состав бетона без модификатора) указывает на высокую трещиностойкость.