PENGARUH VARIASI KONSENTRASI LARUTAN NaAlO2 TERHADAP JENIS ZEOLIT SINTETIS DARI ABU DASAR BATUBARA DENGAN METODE PELEBURAN ALKALI HIDROTERMAL
PENGARUH VARIASI KONSENTRASI LARUTAN NaAlO2 TERHADAP JENIS ZEOLIT SINTETIS DARI ABU DASAR BATUBARA DENGAN METODE PELEBURAN ALKALI HIDROTERMAL
Telah dilakukan sintesis zeolit dari abu dasar batubara menggunakan metode peleburan alkali hidrotermal dengan variasi konsentrasi NaAlO2.Variasi konsentrasi NaAlO2 yang digunakan adalah 2,5 M (Z1), 2 M (Z2), 1,5 M (Z3), dan 1 M (Z4). Abu dasar dan NaOH dilebur selama 3 jam pada suhu 750 C. Sampel kemudian dipanaskan melalui proses hidrotermal dengan medium kristalisasi NaAlO2, Kemudian sampel dinetralkan dengan aquades hingga mencapai pH 9-10. Karakterisasi sampel yang dilakukan meliputi karakterisai jenis zeolit menggunakan XRD dan pengukuran konduktivitas listrik menggunakan LCR-meter. Hasil karaterisasi menggunakan XRD menunjukkan bahwa zeolit yang terbentuk pada sampel Z1, Z2, dan Z3 berupa zeolit jenis sodalit dan pada sampel Z4 zeolit jenis sodalit, nosean, dan megakalsilit. Kemurnian sodalit paling tinggi diperoleh pada sampel Z3, yaitu 73 %. Nilai konduktivitas listrik yang dihasilkan berkisar dari 0,3 x 10-6 – 1,06 x 10-6 S/cm dan berada pada rentang bahan semikonduktor. Zeolit pada sampel Z4 mempunyai konduktivitas listrik tertinggi yaitu 1,06 x 10-6 S/cm. Kata kunci : zeolit, abu dasar, alkali hidrotermal, sodalit, konduktivitas listrik
- Andalas University Indonesia
- Universiti Teknologi MARA Malaysia
- University of Wisconsin–Oshkosh United States
- University of Indonesia Indonesia
- Oxford University Press United Kingdom
QC Physics
QC Physics
Sebayang, P., 2009, Pembuatan Bahan Filter Keramik Berpori Berbasis Zeolit Alam dan Arang Sekam Padi, Teknologi Indonesia, Pusat Peneltian FisikaLIPI, Serpong-Tangerang Selatan, Vol. 32, No. 2, hal. 99-105.
Setyawan, P., 2001, Pengaruh Perlakuan Asam, Hidrotermal, dan Implegnasi Logam Kromium Pada Zeolit Alam dalam Preparasi Katalis, Jurnal Ilmu Dasar, Vol. 3, No.2.
Smallman, R. E. dan Bishop, R. J., 2000, Metalurgi Fisik Modern dan Rekayasa Material, Edisi Keenam, Erlangga, Jakarta.
citations This is an alternative to the "Influence" indicator, which also reflects the overall/total impact of an article in the research community at large, based on the underlying citation network (diachronically).0 popularity This indicator reflects the "current" impact/attention (the "hype") of an article in the research community at large, based on the underlying citation network.Average influence This indicator reflects the overall/total impact of an article in the research community at large, based on the underlying citation network (diachronically).Average impulse This indicator reflects the initial momentum of an article directly after its publication, based on the underlying citation network.Average citations This is an alternative to the "Influence" indicator, which also reflects the overall/total impact of an article in the research community at large, based on the underlying citation network (diachronically).0 popularity This indicator reflects the "current" impact/attention (the "hype") of an article in the research community at large, based on the underlying citation network.Average influence This indicator reflects the overall/total impact of an article in the research community at large, based on the underlying citation network (diachronically).Average impulse This indicator reflects the initial momentum of an article directly after its publication, based on the underlying citation network.Average
Citations provided by BIP!Popularity provided by BIP!- Andalas University Indonesia
- Universiti Teknologi MARA Malaysia
- University of Wisconsin–Oshkosh United States
- University of Indonesia Indonesia
- Oxford University Press United Kingdom
- Oxford University Press
- Universiti Teknologi MARA System Malaysia
- University of Technology Malaysia Malaysia
- Oxford University Press (United Kingdom) United Kingdom
- University of Wisconsin–Madison United States
- University of Indonesia
Telah dilakukan sintesis zeolit dari abu dasar batubara menggunakan metode peleburan alkali hidrotermal dengan variasi konsentrasi NaAlO2.Variasi konsentrasi NaAlO2 yang digunakan adalah 2,5 M (Z1), 2 M (Z2), 1,5 M (Z3), dan 1 M (Z4). Abu dasar dan NaOH dilebur selama 3 jam pada suhu 750 C. Sampel kemudian dipanaskan melalui proses hidrotermal dengan medium kristalisasi NaAlO2, Kemudian sampel dinetralkan dengan aquades hingga mencapai pH 9-10. Karakterisasi sampel yang dilakukan meliputi karakterisai jenis zeolit menggunakan XRD dan pengukuran konduktivitas listrik menggunakan LCR-meter. Hasil karaterisasi menggunakan XRD menunjukkan bahwa zeolit yang terbentuk pada sampel Z1, Z2, dan Z3 berupa zeolit jenis sodalit dan pada sampel Z4 zeolit jenis sodalit, nosean, dan megakalsilit. Kemurnian sodalit paling tinggi diperoleh pada sampel Z3, yaitu 73 %. Nilai konduktivitas listrik yang dihasilkan berkisar dari 0,3 x 10-6 – 1,06 x 10-6 S/cm dan berada pada rentang bahan semikonduktor. Zeolit pada sampel Z4 mempunyai konduktivitas listrik tertinggi yaitu 1,06 x 10-6 S/cm. Kata kunci : zeolit, abu dasar, alkali hidrotermal, sodalit, konduktivitas listrik