Effects of Rare Earth on the Microstructure and Impact Toughness of H13 Steel

Article, Other literature type English OPEN
Gao, Jinzhu; Fu, Paixian; Liu, Hongwei; Li, Dianzhong;
(2015)
  • Publisher: Multidisciplinary Digital Publishing Institute
  • Journal: Metals (issn: 2075-4701)
  • Related identifiers: doi: 10.3390/met5010383
  • Subject: impact toughness | Mining engineering. Metallurgy | rare earth metals (REM) | inclusions | TN1-997 | H13 steel
    mesheuropmc: food and beverages

Studies of H13 steel suggest that under appropriate conditions, additions of rare-earth metals (REM) can significantly enhance mechanical properties, such as impact toughness. This improvement is apparently due to the formation of finer and more dispersive RE inclusion... View more
  • References (32)
    32 references, page 1 of 4

    1. Rafi, H.K.; Ram, G.; Phanikumar, G.; Rao, K.P. Microstructural evolution during friction surfacing of tool steel H13. Mater. Design 2011, 32, 82-87.

    2. Taktak, S. Some mechanical properties of borided AISI H13 and 304 steels. Mater. Design 2007, 28, 1836-1843.

    3. Li, G.; Li, X.; Wu, J. Study of the thermal fatigue crack initial life of H13 and H21 steels. J. Mater. Process. Technol. 1998, 74, 23-26.

    4. Arif, A.; Sheikh, A.; Qamar, S. A study of die failure mechanisms in aluminum extrusion. J. Mater. Process. Technol. 2003, 134, 318-328.

    5. Tsujii, N.; Abe, G.; Fukaura, K.; Sunada, H. High temperature low cycle fatigue behaviour of a 4.2 Cr-2.5 Mo-V-Nb hot work tool steel. J. Mater. Sci. Lett. 1996, 15, 1251-1254.

    6. Hu, X.; Li, L.; Wu, X.; Zhang, M. Coarsening behavior of M23C6 carbides after ageing or thermal fatigue in AISI H13 steel with niobium. Int. J. Fatigue 2006, 28, 175-182.

    7. Sjöström, J. Chromium Martensitic Hot-Work Tool Steels: Damage, Performance and Microstructure. Master Thesis, Karlstad University, Karlstad, Sweden, 2004.

    8. Kchaou, M.; Elleuch, R.; Desplanques, Y.; Boidin, X.; Degallaix, G. Failure mechanisms of H13 die on relation to the forging process-A case study of brass gas valves. Eng. Fail. Anal. 2010, 17, 403-415.

    9. Bahrami, A.; Anijdan, S.; Golozar, M.; Shamanian, M.; Varahram, N. Effects of conventional heat treatment on wear resistance of AISI H13 tool steel. Wear 2005, 258, 846-851.

    10. Rong, W. Fracture analysis on 8407 steel die for Aiuminium pressure-casting. Heat Treat. Met. 2007, 243-245.

  • Metrics
    No metrics available
Share - Bookmark