A two-scale damage model for high cycle fatigue delamination in laminated composites

Article English OPEN
Amiri-Rad, Ahmad; Mashayekhi, Mohammad; van der Meer, Frans P.; Hadavinia, Homa;
(2015)
  • Publisher: Elsevier
  • Subject: mechanical | metallurgy

In this paper a model for predicting fatigue delamination growth in laminated composites under high cycle fatigue is proposed. The model uses the cohesive zone approach and a two-scale continuum damage mechanics model. The behavior of the interface material is considere... View more
  • References (18)
    18 references, page 1 of 2

    [3] B. Yang, S. Mall, K. Ravi-Chandar, A cohesive zone model for fatigue crack growth in quasibrittle materials, International journal of solids and structures 38 (22) (2001) 3927{3944.

    [4] O. Nguyen, E. Repetto, M. Ortiz, R. Radovitzky, A cohesive model of fatigue crack growth, International Journal of Fracture 110 (4) (2001) 351{369.

    [5] K. Roe, T. Siegmund, An irreversible cohesive zone model for interface fatigue crack growth simulation, Engineering fracture mechanics 70 (2) (2003) 209{232.

    [6] P. Robinson, U. Galvanetto, D. Tumino, G. Bellucci, D. Violeau, Numerical simulation of fatigue-driven delamination using interface elements, International journal for numerical methods in engineering 63 (13) (2005) 1824{1848.

    [7] J. Munoz, U. Galvanetto, P. Robinson, On the numerical simulation of fatigue driven delamination with interface elements, International Journal of Fatigue 28 (10) (2006) 1136{ 1146.

    [8] A. Turon, J. Costa, P. Camanho, C. Davila, Simulation of delamination in composites under high-cycle fatigue, Composites Part A: applied science and manufacturing 38 (11) (2007) 2270{2282.

    [9] P. W. Harper, S. R. Hallett, A fatigue degradation law for cohesive interface elements{ development and application to composite materials, International Journal of Fatigue 32 (11) (2010) 1774{1787.

    310 [10] J. Lemaitre, R. Desmorat, Engineering damage mechanics: ductile, creep, fatigue and brittle failures, Springer, 2005.

    [11] J. Lemaitre, I. Doghri, Damage 90: a post processor for crack initiation, Computer methods in applied mechanics and engineering 115 (3) (1994) 197{232.

    [12] J. Lemaitre, J. Sermage, R. Desmorat, A two scale damage concept applied to fatigue, International Journal of Fracture 97 (1-4) (1999) 67{81.

  • Related Organizations (6)
  • Metrics
Share - Bookmark