Wettability between molten slag and dolomitic refractory

Article English OPEN
Shen, Ping ; Zhang, Lifeng ; Wang, Yi ; Sridhar, Seetharaman ; Wang, Qiangqiang (2016)

In the current study, the wettability between molten slag and dolomitic refractory materials used in the ladle during steel refining was investigated. The contact angle between molten slag and dolomitic substrate decreased with increasing temperature. The slag with lower basicity spread on the substrate more easily and penetrated deeper into the substrate. The penetration depth of slag into the refractory increased with the extension of holding time. The CaO in the refractory dissolved into slag which was then saturated with CaO. The reaction between slag and substrate resulted in the formation of solid Ca3SiO5, which slowed down the further penetration of slag into the refractory.\ud \ud
  • References (27)
    27 references, page 1 of 3

    [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] Y. Liang, Y. Li. Slag resistance of MgO-CaO bricks[J]. Refractories, 2009, 43(4): 263-266.

    X. Zhong. Looking ahead-A new generation of high performance refractory ceramics[J]. China's Refractories, 2002, 11(3): 3-13.

    W. Dai, J. Yu. Refractory for clean steel making[J]. Journal of Materials and Metallurgy, 2003, 2(1): 3-9.

    Z. Li, S. Zhang, W. E. Lee. Improving the hydration resistance of lime-based refractory materials[J]. International Materials Reviews, 2008, 53(1): 1-20.

    H. Zhang, H. Zhao, J. Chen, et al. Defect study of MgO-CaO material doped with CeO2[J].

    Advances in Materials Science and Engineering, 2013, 10(4): 1-5.

    M. Chen, C. Lu, J. Yu. Improvement in performance of MgO-CaO refractories by addition of nano-sized ZrO2[J]. Journal of the European Ceramic Society, 2007, 27(16): 4633-4638.

    Journal of Iron and Steel Research, 2004, 16(1): 10-14.

    F. Kashaninia, H. Sarpoolaky, A. R. Bagheri, et al. Improving hydration resistance of magnesiadoloma refractories byiron oxide addition[J]. Iranian Journal of Materials Science and Engineering, 2011, 8(4): 34-40.

    A. G. T. Martinez, M. A. Camerucci, A. L. Cavalieri, et al. Sintering behavior of periclase-doloma refractory mixes[J]. Journal of the European Ceramic Society, 2009, 29(4): 581-586.

  • Metrics
    0
    views in OpenAIRE
    0
    views in local repository
    18
    downloads in local repository

    The information is available from the following content providers:

    From Number Of Views Number Of Downloads
    Warwick Research Archives Portal Repository - IRUS-UK 0 18
Share - Bookmark